67 comparison of tribological behaviour of tin ticn and

2020-6-15Comparison of TiN and Ti1−xAlxN coatings deposited on Al using plasma immersion ion implantation assisted deposition 5 Comparison of TiO2 nanoparticles impact with TiO2/CNTs nano hybrid on microbial community of staphylococcus 6 Abrasive and erosive properties of coal can lead to serious operational problems in mining industry Here the abrasive medium is varied containing often fractions of quartz pyrite and contents of coal which can be also mixed with water resulting in an abrasive slurry mixture A better understanding of the dependence between the environmental and systematic conditions of the tribological

Investigation of tribological properties of coated high

The demand for weight reduction in vehicles has increased significantly over the last ten years since the new regulations for CO2 emissions control were introduced Furthermore the enhanced safety requirements have promoted the development of new materials with high strength-to-weight ratio such as the high strength steel (HSS) formed at high temperatures

The demand for weight reduction in vehicles has increased significantly over the last ten years since the new regulations for CO2 emissions control were introduced Furthermore the enhanced safety requirements have promoted the development of new materials with high strength-to-weight ratio such as the high strength steel (HSS) formed at high temperatures

The demand for weight reduction in vehicles has increased significantly over the last ten years since the new regulations for CO2 emissions control were introduced Furthermore the enhanced safety requirements have promoted the development of new materials with high strength-to-weight ratio such as the high strength steel (HSS) formed at high temperatures

2012-2-20In addition the TiN/TiCN multilayer thick film showed different types of tribological behaviour against Si 3 N 4 balls and steel balls The mean coefficient of friction and the wear rate of the film were about 0 14 and 1 15 10 −6 mm 3 N −1 m −1 when the film slid against Si 3 N 4 balls for 1 h

2012-11-13Alm de obter melhores propriedades tribomecnicas e resistncia a corroso os revestimentos de TiC TiN e TiCxN1-x so excelentes candidatos para fabricao de implantes por serem biocompatveis(3) O TiCxN1-x uma soluo slida de TiN + TiC portanto este filme incorpora as caractersticas de ambas as fases presentes(4)

Adhesion and Corrosion of Ti TiN and TiCrN Films

Abstract In the present work several films of Ti TiN and TiCrN have been coated on AISI 316L stainless steel substrates using magnetron sputtering techniques in order to improve their surface properties The morphology and structure of the coatings were analysed using scanning electron microscopy (SEM) and X-ray diffraction (XRD) The electrochemical performances skills in an SBF solution

2005-4-11 Introduction Mechanical properties and tribological parameters of TiN coatings were exhaustively studied and are often regarded as references Wear performance of TiN coatings at elevated temperatures was studied in Ref where the effect of increased temperature on the behaviour of a TiN coated stainless steel in dry sliding contact against a Si 3 N 4 ceramic ball was reported

Tribological properties of transition metal di-chalcogenide based lubricant coatings Tribological properties of transition metal di-chalcogenide based lubricant coatings Jun-Feng YANG 1 2 Braham PARAKASH 1 Jens HARDELL 1 Qian-Feng FANG 2 1

2018-7-2Manganese Additions and Wear Parameter on the Tribological Behaviour of NFGrey (8) Cast Iron' Tribology in Industry vol 34 no 4 pp 239-246 3 Ahn SH Yoo JH Kim JG Han JG 2003 'On the corrosion behavior of multilayered WC–Ti1yxAlxN coatings on AISI D2 steel'

Tribological characterisation along with 3D surface profile of wear track of (a) uncoated (b) CVD bilayer TiCN/Al O coated and (c) PVD multilayer TiAlN/TiN 2 3 coated tools mode while the coated tools were studied using grazing incidence grain boundaries can also be captured from the figure

2020-6-15Comparison of TiN and Ti1−xAlxN coatings deposited on Al using plasma immersion ion implantation assisted deposition 5 Comparison of TiO2 nanoparticles impact with TiO2/CNTs nano hybrid on microbial community of staphylococcus 6

2008-10-8TiN used as a hard coating is chemically inert which in turn provides a good corrosion protection When producing the TiN coatings on the substrate surface some defects such as pores or cracks may occur which leads to a pitting and delamination of the surface [12 13 and 14]

Tribological behaviour of nanodiamond reinforced UHMWPE in water-lubricated contacts A Golchin A Villain N Emami Tribology International – Volume 110 June 2017 Pages 195-200 TE 67 Paper # 1147 : Tribological behaviour of an electrochemical jet machined textured Al-Si automotive cylinder liner material

Development and tribo

2020-6-2567 Prengel H Madaoui N Saoula N Zaid B et al Structural mechanical and electrochemical comparison of TiN and TiCN coatings on XC48 steel substrates in NaCl 3 5% water solution The effect of boron additions on the tribological behaviour of TiN coatings produced by electron-beam evaporative PVD

Its mechanical and tribological properties can be further improved by alloying it with carbon (W-S-C films) These films are commonly manufactured by sputter deposition The present work investigates the influence of sputtering procedure on the microtribological performance of W-S-C films

Comparison of three-dimensional scanner systems for craniomaxillofacial imaging Aplikazio ortopedikoetarako TiN eta TiCN-rekin estalduriko Titanio aleazioen portaera tribologikoa Tribological behaviour of CpTi and Ti-6Al-4V alloys coated by TiN and TiCN against UHMWPE

CN103785600A CN201410030135 2A CN201410030135A CN103785600A CN 103785600 A CN103785600 A CN 103785600A CN 201410030135 A CN201410030135 A CN 201410030135A CN 103785600 A CN103785600 A CN 103785600A Authority CN China Prior art keywords surface steel abrasion thin films sodium hydroxide Prior art date 2014-01-23 Application number CN201410030135 2A

Antunes RA De Assis S Lorenzetti SG ZazucoHiga O Costa I Comparison of in vitro corrosion behaviour and biocompatibility of Ti-13zr-13nb and passivated 316l stainless steel coated with TiCN Presented at the 18th International Congress Of Mechanical Engineering Ouro

The tribological behaviors and wear mechanisms between Al/hBN coatings and Ni/cBN or Ni/Si3N4 abrasive coatings were investigated Results shown that after a period of efficient cutting bare blade and Ni/cBN coating were covered by different degrees of transfer materials while no obvious transfer layer was detected on Ni/Si3N4 coating

This work employs the PVD process to deposit coatings of single layer TiN binary layer TiN/TiCN multilayer TiN⇔⇔N and sequenced TiN⇔CN⇔N multilayer coatings with variable individual TiN-layer and TiCN-layer thicknesses on tungsten carbide disks and inserts Also investigated are the fracture mechanisms and the influence of sequence and thickness of these coatings on cylinder-on-disk

2016-10-27TiCN/TiN TiN/TiC Ti/TiN) where the TiN layer is usually deposited first because it adheres very firmly to different substrates (e g HSS silicon) [6 7] Due to brittleness and its poor a dherence of TiC layer most studies concern about TiN/Ti(C N)/TiC [810]